美国SABIC阻燃PPO树脂NORYL N190X
UL Yellow Card1 |
|
Density / Specific Gravity | 1.13 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR)(280°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR)(280°C/5.0 kg) | 23 | cm/10min | *** 1133 |
Molding Shrinkage - Flow(3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Water Absorption(24 hr) | 0.080 | % | ASTM D570 |
Outdoor Suitability | f1 | UL 746C | |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 120 | ASTM D785 |
Charpy Notched Impact Strength(23°C) | 20 | kJ/m | *** 179/2C |
Notched Izod Impact | |||
-30°C | 100 | J/m | ASTM D256 |
23°C | 290 | J/m | ASTM D256 |
23°C8 | 20 | kJ/m | *** 180/1A |
Unnotched Izod Impact(23°C) | 720 | J/m | ASTM D4812 |
Instrumented Dart Impact(23°C, Total Energy) | 50.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | 95.0 | °C | *** 75-2/Bf |
1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | 82.0 | °C | *** 75-2/Af |
Flame Rating | UL 94 | ||
1.0 mm | HB | ||
1.5 mm | V-0 | ||
3.0 mm | 5VA | ||
Oxygen Index | 39 | % | ASTM D2863 |
PPO性能
1、PPO综合性能良好，可在120度蒸汽中使用，电绝缘性好，吸水小，但有应力开裂倾向。改性聚苯醚可消除应力开裂。
2、有突出的电绝缘性和耐水性***，有较好的***性和电性能，尺寸稳定性好。其介电性能居塑料的首位。
3、MPPO为PPO与HIPS共混制得的改性材料，市面上的材料均为此种材料。
4、PPO有较高的耐热性，玻璃化温度211度，熔点268度，加热至330度有分解倾向，PPO的含量越高其耐热性越好，热变形温度可达190度。