美国SABIC玻纤10%增强PPE/PA NORYL GTX810

Density / Specific Gravity	1.16 1.16	g/cm	ASTM D792
Molding Shrinkage			Internal Method
Across Flow : 3.20 mm	0.65 to 0.85	%
Flow : 3.20 mm	0.60 to 0.80	%
Water Absorption			ASTM D570
24 hr, 50% RH	0.50	%
Equilibrium, 50% RH	1.0	%
Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness(R-Scale)	119		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength2			ASTM D638
Yield	89.0	MPa
Break	88.0	MPa
Tensile Elongation3(Break)	10	%	ASTM D638
Flexural Modulus4(100 mm Span)	3960	MPa	ASTM D790
Flexural Strength4(Yield, 100 mm Span)	155	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-30°C	53	J/m
23°C	80	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, 6.40 mm	245	°C
1.8 MPa, Unannealed, 6.40 mm	210	°C
Vicat Softening Temperature	240	°C	ASTM D15255