| Specific Gravity | 1.15g/cc | 1.15g/cc | ASTM D792 |
| Density | 1.15g/cc | 0.0415lb/in | ISO 1183 |
| Moisture Absorption | 0.350 % | 0.350 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060-0.0080cm/cm @Thickness 3.20 mm | 0.0060-0.0080in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 26.3g/10 min @Load 5.00 kg, Temperature 280 °C | 26.3g/10 min @Load 11.0 lb, Temperature 536 °F | ASTM D1238 |
| Melt Index of Compound | 22g/10 min @Load 5.00 kg, Temperature 280 °C | 22g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 |
| Tensile Strength at Break | 80.0MPa | 11600psi | Type I, 5 mm/min; ASTM D638 |
| 82.0MPa | 11900psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 84.0MPa | 12200psi | Type I, 5 mm/min; ASTM D638 |
| 87.0MPa | 12600psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| 10.2 % | 10.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.3 % | 4.3 % | Type I, 5 mm/min; ASTM D638 |
| 4.5 % | 4.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.56GPa | 516ksi | 5 mm/min; ASTM D638 |
| 4.00GPa | 580ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0MPa | 13300psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 133MPa | 19300psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 3.32GPa | 482ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.52GPa | 511ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.820J/cm | 1.54ft-lb/in | ASTM D256 |
| 0.450J/cm @Temperature -30.0 °C | 0.843ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00kJ/m | 3.33ft-lb/in | 80*10*4; ISO 180/1A |
| 3.00kJ/m @Temperature -30.0 °C | 1.43ft-lb/in @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.800J/cm | 3.81ft-lb/in | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 4.00J @Temperature 23.0 °C | 2.95ft-lb @Temperature 73.4 °F | ASTM D3763 |
PPO性能
1、PPO综合性能良好，可在120度蒸汽中使用，电绝缘性好，吸水小，但有应力开裂倾向。改性聚苯醚可消除应力开裂。
2、有突出的电绝缘性和耐水性***，有较好的***性和电性能，尺寸稳定性好。其介电性能居塑料的首位。
3、MPPO为PPO与HIPS共混制得的改性材料，市面上的材料均为此种材料。
4、PPO有较高的耐热性，玻璃化温度211度，熔点268度，加热至330度有分解倾向，PPO的含量越高其耐热性越好，热变形温度可达190度。
5、PPO阻燃性良好，具有自息性，与HIPS混合后具有中等可燃性。质轻，***可用于食品和***行业。耐光性差，长时间在阳光下使用会变色。