经销沙伯基础***高抗冲PPO/PA NORYL GTX964W
| 比重 | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| 平衡吸湿 | 1.19 % | 1.19 % | 50% RH; ASTM D570 |
| 3.5 % | 3.5 % | ASTM D570 | |
| 线性成型收缩率,Flow | 0.015 cm/cm | 0.015 in/in | SABIC Method |
| 线性成型收缩率，横向 | 0.013 cm/cm | 0.013 in/in | SABIC Method |
| 化合物熔体指数 | 7.0 g/10 min @Load 2.16 kg, Temperature 280 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 536 °F | MVR [cm^3/10 min]; *** 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 45.0 MPa | 6530 psi | 50 mm/min; *** 527 |
| 抗张强度(屈服) | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 50 mm/min; *** 527 | |
| 伸长率 (断裂) | 50 % | 50 % | 50 mm/min; *** 527 |
| 56 % | 56 % | Type I, 50 mm/min; ASTM D638 | |
| 屈服伸长率 | 4.0 % | 4.0 % | 50 mm/min; *** 527 |
| 弯曲强度 | 70.0 MPa | 10200 psi | 2 mm/min; *** 178 |
| 载荷下热变形温度(0.46 MPa) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; *** 75/Be |
| 185 °C @Thickness 6.40 mm | 365 °F @Thickness 0.252 in | unannealed; ASTM D648 | |
| 维卡软化温度 | 175 °C | 347 °F | Rate B/50; *** 306 |
| 180 °C | 356 °F | Rate B/120; *** 306 | |
| 240 °C | 464 °F | Rate A/50; *** 306 |