40%GF增韧PPS Torelina A674M2
¥55.50
65%玻矿PPS Torelina A310MX04
¥55.50
70%玻矿低翘曲PPS Torelina A310M
¥55.50
高流动高钢PPS Torelina A305MD1
¥55.50
PPS Torelina A400MX01高流动玻矿增强
¥55.50
批发深圳东丽耐湿热30%玻纤PPS Torelina A673M-T
Density(23°C) | 1.52 | g/cm | *** 1183 |
Molding Shrinkage2 | Internal Method | ||
Across Flow : 3.00 mm | 0.85 | % | |
Flow : 3.00 mm | 0.20 | % | |
Water Absorption(24 hr, 23°C) | 0.020 | % | *** 62 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 114 | *** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress(23°C) | 150 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 2.5 | % | *** 527-2 |
Flexural Modulus(23°C) | 10000 | MPa | *** 178 |
Flexural Stress(23°C) | 225 | MPa | *** 178 |
Shear Strength(23°C) | 68.0 | MPa | JIS K7214 |
Taber Abrasion Resistance(1000 Cycles) | 50.0 | mg | *** 9352 |
Coefficient of Friction - vs. Metal | 0.25 | ||
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 14 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 60 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 255 | °C | *** 75-2/A |
Melting Temperature | 278 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow | 2.2E-5 | cm/cm/°C | |
Transverse | 3.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength | 26 | kV/mm | IEC 60243-1 |
Dielectric Constant(23°C, 1 MHz) | 3.80 | IEC 60250 | |
Dissipation Factor(23°C, 1 MHz) | 2.0E-3 | IEC 60250 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating(1.5 mm) | V-0 | UL 94 |