产品详情
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 |
机械性能 | 拉伸强度(引张强度) |
| ASTM D638/ISO 527 | 22 | kg/cm2(MPa)[Lb/in2] |
断裂伸长率 |
| ASTM D638/ISO 527 |
| % |
拉伸模量 |
| ASTM D638/ISO 527 |
| kg/cm2(MPa)[Lb/in2] |
拉伸屈服伸长率(延伸率) |
| ASTM D638/ISO 527 |
| % |
拉伸断裂伸长率(延伸率) |
| ASTM D638/ISO 527 |
| % |
弯曲模量(弯曲弹性率) |
| ASTM D790/ISO 178 | 2.1 | kg/cm2(MPa)[Lb/in2] |
弯曲强度 |
| ASTM D790/ISO 178 | 29 | kg/cm2(MPa)[Lb/in2] |
洛氏硬度 |
| ASTM D785 |
|
|
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
1/4" -30℃ | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
1/8" 23℃ | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
1/8" -30℃ | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
-30℃(缺口) | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
23℃(无缺口) | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
-30℃(无缺口) | ASTM D256/ISO 179 |
| kg·cm/cm(J/M)ft·lb/in |
物性性能 | 比重(密度) |
| ASTM D792/ISO 1183 | 1.68 |
|
成型收缩率 |
| ASTM D955 |
| % |
熔融指数(流动系数) | 200℃/5kg | ASTM D1238/ISO 1133 |
| g/10min |
220℃/10kg | ASTM D1238/ISO 1133 |
| g/10min |
吸水率 23℃/24H |
| ASTM D570/ISO 62 | 0.02 | % |
热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | >500 | ℃(℉) |
未退火 | ASTM D648/ISO 75 |
| ℃(℉) |
维卡软化点 |
| ASTM D1525/ISO R306 |
| ℃(℉) |
熔点 |
| - |
| ℃(℉) |
燃烧性(率) |
| UL94 |
|
|
线性膨胀系数 |
| ASTM D696/ISO 11359 |
| mm/mm.℃ |
电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 |
|
|
1MHZ | ASTM D150/IEC 60250 |
|
|
体积电阻率 |
| ASTM D257/IEC 60093 | 1*10^16 | Ω.cm |
表面电阻率 |
| ASTM D257/IEC 60093 |
| Ω |
耐电弧性 |
| ISO 14782 | 125 |
|
加工条件 | 干燥条件 |
|
|
|
|
加工温度 | 射嘴 |
|
| ℃ |
料筒前段 |
|
| ℃ |
料筒中段 |
|
| ℃ |
料筒后段 |
|
| ℃ |
熔体温度 |
|
|
| ℃ |
模具温度 |
|
|
| ℃ |
压力 | 注塑压力 |
|
| Mpa |
保压压力 |
|
| Mpa |
背压 |
|
| Mpa |
螺杆转速 |
|
|
| rpm |
其他 | 备注 |
|
颜色 | 黑色 |
特性 | 高温下耐化学和机械性能 |
用途 |
|
产品参数
- 注塑级
- 否
- 美国
- 美国菲利普
- PPS
- 品牌经销
- 标准料
- R-4-02
- PPS
- 注塑级
- 标准级
- 通用级
- 美国菲利普
- 25
- PPS/美国雪佛龙菲利普斯/R-4-02 加40%玻纤 阻燃V0
- ¥33.30