注塑级 PPS QA221N 美国苏威涂覆用

¥55.00 ≥1千克起批

参数

否是否进口
美国产地
美国苏威厂家(产地)

发货地广东东莞 1天内发货供货总量18000千克

东莞市樟木头双浩塑胶原料经营部 2年: 进入店铺在线咨询

PPS粉末 Ryton QA321N PPS QA281N 美国苏威高流动性粉末涂料 ¥60.00

高粘度PPS粉 Ryton QC160P PPS QC160N 美国苏威注塑挤出级 ¥60.00

Ryton QC200N PPS QC200P 美国苏威 PPS粉 PPS树脂颗粒 ¥55.00

注塑级PPS颗粒 Ryton QC210P PPS粉末 QC210N 美国苏威 ¥55.00

Ryton QC220N PPS QC220P 美国苏威注塑挤出涂层 ¥55.00

PPS粉末 Ryton QC230N 美国苏威高分子量聚苯硫醚拉丝级 ¥55.00

产品详情

Physical Properties	Metric	English	Comments

Density	1.34 g/cc	0.0484 lb/in³	ASTM D792
Volatiles	<= 0.30 % @Temperature 150 °C	<= 0.30 % @Temperature 302 °F
Water Absorption	0.050 % @Time 86400 sec	0.050 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.010 cm/cm @Thickness 3.20 mm	0.010 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	160 g/10 min	160 g/10 min	Procedure B; ASTM D1238
Ash	0.10 %	0.10 %

Mechanical Properties	Metric	English	Comments
Tensile Stress	80.0 MPa	11600 psi	*** 527-2
Elongation at Break	4.0 %	4.0 %	*** 527-2
Tensile Modulus	3.40 GPa	493 ksi	*** 527-2
Flexural Strength	140 MPa	20300 psi	*** 178
Flexural Modulus	3.40 GPa	493 ksi	*** 178
Izod Impact, Notched	0.530 J/cm @Thickness 3.18 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (***)	4.00 kJ/m²	1.90 ft-lb/in²	Notch A; *** 180

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	24.0 kV/mm	610 kV/in	ASTM D149
Dissipation Factor	0.0020 @Frequency 1.00e+6 Hz	0.0020 @Frequency 1.00e+6 Hz	ASTM D150

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C @Temperature -50.0 - 50.0 °C	27.8 µin/in-°F @Temperature -58.0 - 122 °F	ASTM E831
	120 µm/m-°C @Temperature 100 - 200 °C	66.7 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Thermal Conductivity	0.290 W/m-K	2.01 BTU-in/hr-ft²-°F	ASTM C177
Melting Point	280 °C	536 °F	*** 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	95.0 °C	203 °F	Unannealed; ASTM D648
Vicat Softening Point	>= 180 °C	>= 356 °F	*** 306
Glass Transition Temp, Tg	90.0 °C	194 °F	*** 11357-2
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
Oxygen Index	44 %	44 %	ASTM D2863