PSU GZ004 加磨砂玻璃20% 低翘曲

¥90.00 ≥1千克起批

参数

否是否进口
美国产地
沙伯基础(原GE)厂家(产地)

发货地广东东莞 1天内发货供货总量30000千克

东莞市樟木头双浩塑胶原料经营部 3年: 进入店铺在线咨询

PEEK LCL33 沙伯基础 15%碳纤维 15%PTFE 耐磨导电 ¥90.00

PEEK LCL33E 沙伯基础(原GE) 15%碳纤维 15%PTFE 耐磨导电易于成型 ¥90.00

PEI LCL33EXQ 15%碳纤维 15%PTFE 耐磨导电易于成型 ¥90.00

PSU LCL36 30%碳纤维 15%PTFE 耐磨导电润滑 ¥104.00

PEEK LCL36E 沙伯基础(原GE) 30%碳纤维15%PTFE 高强度导电 ¥480.00

PEEK LFL36E 沙伯基础(原GE) 好的成型性能润滑加玻纤30% 低摩擦系数 ¥450.00

产品详情

Physical Properties	Metric	English	Comments

Density	1.35 g/cc	0.0488 lb/in³	*** 1183
Moisture Absorption	<= 0.0500 %	<= 0.0500 %	Injection Molding
Moisture Absorption at Equilibrium	0.10 - 0.30 %	0.10 - 0.30 %	23°C/50% RH; *** 62-4
Water Absorption at Saturation	0.50 - 0.60 %	0.50 - 0.60 %	*** 62-1
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	SABIC method
Linear Mold Shrinkage, Transverse	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	SABIC method

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	57.0 MPa	8270 psi	5 mm/min; *** 527
Elongation at Break	5.0 %	5.0 %	5 mm/min; *** 527
Elongation at Yield	3.6 %	3.6 %	5 mm/min; *** 527
Tensile Modulus	3.70 GPa	537 ksi	1 mm/min; *** 527
Flexural Strength	104 MPa	15100 psi	break, 2mm/min; *** 178
Flexural Modulus	3.60 GPa	522 ksi	2 mm/min; *** 178
Izod Impact, Notched (***)	5.00 kJ/m²	2.38 ft-lb/in²	80104; *** 180/1A
Izod Impact, Unnotched (***)	40.0 kJ/m²	19.0 ft-lb/in²	80104; *** 180/1U
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	Edgew 80104 sp=62mm; *** 179/1eU
Charpy Impact, Notched	0.700 J/cm²	3.33 ft-lb/in²	Edgew 80104 sp=62mm; *** 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	49.0 µm/m-°C @Temperature -40.0 - 40.0 °C	27.2 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E831
CTE, linear, Transverse to Flow	52.0 µm/m-°C @Temperature -40.0 - 40.0 °C	28.9 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E831
Deflection Temperature at 0.46 MPa (66 psi)	181 °C	358 °F	Flatw 80104 sp=64mm; *** 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	170 °C	338 °F	Flatw 80104 sp=64mm; *** 75/Af
Vicat Softening Point	186 °C	367 °F	Rate B/50; *** 306
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in	UL 94

Processing Properties	Metric	English	Comments
Nozzle Temperature	340 - 370 °C	644 - 698 °F
Zone 2	340 - 350 °C	644 - 662 °F
Zone 3	350 - 360 °C	662 - 680 °F
Melt Temperature	360 - 370 °C	680 - 698 °F	Injection Molding
Mold Temperature	150 °C	302 °F
Drying Temperature	120 - 150 °C	248 - 302 °F	Injection Molding
Dry Time	4.00 hour	4.00 hour	Injection Molding
Back Pressure	0.200 - 0.300 MPa	29.0 - 43.5 psi

本公司长期销售沙伯基础 PEI，ABS，ASA，EVA，PA6，PBT，PE，PBT，PET，PMMA，POM，PS，PP，PU，PES，PC料等多种牌号

我司产品均可提供详细物性表(英文和中文版)相关资料；可开13%增值税发票；免费为客户分析样版并提供原料型号咨询服务(可免费帮客户翻译英文资料)；如需试料、了解产品相关信息及当日报价，敬请来电、竭诚为您服务！