LNP THERMOCOMP EC004XXC 含有20%碳纤维的聚醚酰亚胺树脂
- ¥98.00 ≥25千克起批
- 否是否进口
- 中国厂家(产地)
- EC004XXC牌号
MECHANICAL1)Tensile Stress, break170MPaASTM D638Tensile Strain, break2%ASTM D638Flexural Stress259MPaASTM D790Flexural Modulus12330MPaASTM D790Tensile Stress, break175MPaISO 527Tensile Strain, break2%ISO 527Tensile Modulus, 1 mm/min14500MPaISO 527Flexural Stress250MPaISO 178Flexural Modulus12000MPaISO 178IMPACT1)Izod Impact, unnotched, 23°C534J/mASTM D4812Izod Impact, notched, 23°C53J/mASTM D256Izod Impact, unnotched 80*10*4 +23°C30kJ/m²ISO 180/1UIzod Impact, notched 80*10*4 +23°C7kJ/m²ISO 180/1ATHERMAL1)HDT, 1.82 MPa, 3.2mm, unannealed212°CASTM D648CTE, -40°C to 40°C, flow1.E-051/°CISO 11359-2CTE, -40°C to 40°C, xflow6.E-051/°CISO 11359-2HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm210°CISO 75/AfPHYSICAL1)Density1.34g/cm³ASTM D792Mold Shrinkage, flow, 24 hrs3)0.1-0.3%ASTM D955Mold Shrinkage, xflow, 24 hrs3)0.3-0.5%ASTM D955Mold Shrinkage, flow, 24 hrs3)0.1-0.3%ISO 294Mold Shrinkage, xflow, 24 hrs3)0.3-0.5%ISO 294Density1.34g/cm³ISO 1183Moisture Absorption (23°C / 50% RH)0.2%ISO 62ELECTRICAL1)Surface Resistivity1.E+02-1.E+06ΩASTM D257INJECTION MOLDING2)Drying Temperature150°CDrying Time4-6HrsMaximum Moisture Content0.02%Melt Temperature360-400°CRear - Zone 1 Temperature360-380°CMiddle - Zone 2 Temperature370-390°CFront - Zone 3 Temperature380-400°CNozzle Temperature390-400°CMold Temperature140-180°CBack Pressure0.3-0.7MPaScrew speed (Circumferential speed)0.2-0.3m/sVent Depth0.025-0.076mmFLAME CHARACTERISTICS1)UL Compliant, 94V-0 Flame Class Rating4)0.5mmUL 94 by SABIC-IP
在线问
- 否
- 中国
- EC004XXC
- 注塑