LNP THERMOCOMP RC004SXS 热稳定、导电
¥118.00
- 商品
- 详情
LNP THERMOCOMP RC004SXC 含有碳纤维的PA66树脂
- ¥118.00 ≥25千克起批
参数
- 否是否进口
- 中国厂家(产地)
- RC004SXC 牌号
广东 东莞
不限
LNP THERMOCOMP RC004SXS 热稳定、导电
¥118.00
产品详情
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break, 5 mm/min | 200 | MPa | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 | |
| Flexural Stress, break, 2 mm/min | 269 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 10500 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A | |
| THERMAL | 1) | |||
| CTE, 23°C to 60°C, flow | 1.7E-05 | 1/°C | ISO 11359-2 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 250 | °C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Mold Shrinkage, flow | 3) | 0.1-0.3 | % | SABIC method |
| Density | 1.22 | g/cm³ | ISO 1183 | |
| ELECTRICAL | 1) | |||
| Surface Resistivity | 1.E+02-1.E+04 | Ω | ASTM D257 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 80 | °C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 280-305 | °C | ||
| Front - Zone 3 Temperature | 295-305 | °C | ||
| Middle - Zone 2 Temperature | 280-295 | °C | ||
| Rear - Zone 1 Temperature | 265-275 | °C | ||
| Mold Temperature | 95-110 | °C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |