| PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
|---|
| MECHANICAL | 1) |
|
|
|
|---|
| Tensile Stress, yield, 5 mm/min |
| 120 | MPa | ISO 527 |
|---|
| Tensile Strain, break, 5 mm/min |
| 2 | % | ISO 527 |
|---|
| Flexural Stress, yield, 2 mm/min |
| 160 | MPa | ISO 178 |
|---|
| Flexural Modulus, 2 mm/min |
| 5000 | MPa | ISO 178 |
|---|
| IMPACT | 1) |
|
|
|
|---|
| Izod Impact, unnotched 80*10*4 +23°C |
| 30 | kJ/m² | ISO 180/1U |
|---|
| Izod Impact, notched 80*10*4 +23°C |
| 5 | kJ/m² | ISO 180/1A |
|---|
| THERMAL | 1) |
|
|
|
|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
| 275 | °C | ISO 75/Af |
|---|
| PHYSICAL | 1) |
|
|
|
|---|
| Mold Shrinkage, flow | 3) | 0.5-0.7 | % | SABIC method |
|---|
| Density |
| 1.29 | g/cm³ | ISO 1183 |
|---|
| INJECTION MOLDING | 2) |
|
|
|
|---|
| Drying Temperature |
| 120-150 | °C |
|
|---|
| Drying Time |
| 4 | Hrs |
|
|---|
| Maximum Moisture Content |
| 0.15 | % |
|
|---|
| Melt Temperature |
| 315-330 | °C |
|
|---|
| Front - Zone 3 Temperature |
| 325-340 | °C |
|
|---|
| Middle - Zone 2 Temperature |
| 315-325 | °C |
|
|---|
| Rear - Zone 1 Temperature |
| 310-320 | °C |
|
|---|
| Mold Temperature |
| 140-165 | °C |
|
|---|
| Back Pressure |
| 0.2-0.3 | MPa |
|
|---|
| Screw Speed |
| 30-60 | rpm |
|
|---|