LNP THERMOCOMP ZF0089 含有40%玻璃纤维的PPO树脂

¥118.00 ≥25千克起批

参数

否是否进口
中国厂家(产地)
ZF0089牌号

发货地广东东莞不限

东莞市聚浩塑化有限公司 2年: 进入店铺在线咨询

LNP THERMOCOMP ZFM3314 ¥118.00

LNP THERMOCOMP ZFM62P ¥118.00

LNP Thermocomp ZKC04 ¥198.00

LNP Thermocomp ZKC06 含有矿物填料和抗冲改性剂 ¥78.00

LNP THERMOCOMP ZX06323 ¥118.00

LNP THERMOCOMP ZX08005 基于PPE+PS共混树脂 ¥118.00

产品详情

PROPERTIES		TYPICAL VALUES	UNITS	TEST METHODS
MECHANICAL	¹⁾
Tensile Stress, brk, Type I, 5 mm/min		101	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min		1	%	ASTM D638
Tensile Modulus, 50 mm/min		13020	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span		131	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span		11800	MPa	ASTM D790
Tensile Strain, break, 5 mm/min		0.8	%	ISO 527
Tensile Modulus, 1 mm/min		12280	MPa	ISO 527
Flexural Modulus, 2 mm/min		11940	MPa	ISO 178
IMPACT	¹⁾
Izod Impact, unnotched, 23°C		332	J/m	ASTM D4812
Izod Impact, notched, 23°C		74	J/m	ASTM D256
Multiaxial Impact		3	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C		12	J	ASTM D3763
Izod Impact, unnotched 80104 +23°C		19	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C		6	kJ/m²	ISO 180/1A
THERMAL	¹⁾
HDT, 0.45 MPa, 3.2 mm, unannealed		110	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed		103	°C	ASTM D648
CTE, -30°C to 30°C, flow		3.1E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow		5.4E-05	1/°C	ASTM D696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm		112	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm		105	°C	ISO 75/Af
PHYSICAL	¹⁾
Specific Gravity		1.52	-	ASTM D792
Density		1.52	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)		0.07	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	³⁾	0.2-0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	³⁾	0.5-0.8	%	ASTM D955
Density		1.51	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)		0.09	%	ISO 62
INJECTION MOLDING	²⁾
Drying Temperature		120	°C
Drying Time		4	Hrs
Melt Temperature		300-305	°C
Front - Zone 3 Temperature		300-310	°C
Middle - Zone 2 Temperature		290-300	°C
Rear - Zone 1 Temperature		275-290	°C
Mold Temperature		80-110	°C
Back Pressure		0.2-0.3	MPa
Screw Speed		30-60	rpm

为您推荐

LNP THERMOCOMP ZX08309 ¥118.00
LNP THERMOTUF DF002PSI 玻璃增强聚碳酸酯 ¥68.00
LNP THERMOTUF DF008EI 易于成型、脱模、高冲击 ¥118.00
LNP THERMOTUF ENH2900A 无氯化、无溴阻燃的PC+PBT树脂 ¥118.00
LNP THERMOTUF IX02582 高冲击性 PA612 ¥118.00
LNP THERMOTUF MF004AI 含有20%玻璃纤维的聚丙烯树脂 ¥118.00

LNP THERMOTUF MX00619 ¥118.00
LNP THERMOTUF OF006I 高冲击性 ¥120.00
LNP THERMOTUF OF008EI ¥118.00
LNP THERMOTUF OF008I 基于PPS线性树脂的含有玻璃纤维 ¥118.00
LNP THEMROTUF PF003IU 具有抗冲改性剂和紫外线稳定 ¥118.00
LNP THERMOTUF PF006I 含有30%玻璃纤维的尼龙6树脂 ¥112.00

LNP THERMOTUF PF008IR 含有40%玻璃纤维的尼龙6树脂 ¥75.00
LNP THERMOTUF PX06416 含有15%玻璃纤维的尼龙6树脂 ¥118.00
LNP THERMOTUF PX06417 含有40%玻璃纤维的尼龙6树脂 ¥118.00
LNP THERMOTUF PX95726 ¥78.00
LNP THERMOTUF QX01581H 玻璃纤维的尼龙6/10树脂 ¥78.00
LNP THERMOTUF R1000I 含有抗冲改性剂的尼龙66树脂 ¥118.00

供应商网> 特种塑料> LNP THERMOCOMP ZF0089 含有40%玻璃纤维的PPO树脂

在线问

产品参数

是否进口否
厂家(产地)中国
牌号ZF0089
用途级别注塑

1/2

¥118.00 在线咨询

进店客服获取最低报价拨打电话

LNP THERMOCOMP ZF0089 含有40%玻璃纤维的PPO树脂: ¥118.00