FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E45329-101358095 | - | - |
---|
UL Recognized, 94HB Flame Class Rating | 1) | 1.5 | mm | UL 94 |
---|
MECHANICAL | 2) |
|
|
|
---|
Tensile Modulus, 5 mm/min |
| 10440 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 5 mm/min |
| 131 | MPa | ASTM D638 |
---|
Tensile Strain, brk, Type I, 5 mm/min |
| 1.8 | % | ASTM D638 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 9350 | MPa | ASTM D790 |
---|
Flexural Stress, brk, 1.3 mm/min, 50 mm span |
| 190 | MPa | ASTM D790 |
---|
Tensile Stress, break, 5 mm/min |
| 140 | MPa | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 1.5 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 14000 | MPa | ISO 527 |
---|
Flexural Stress, break, 2 mm/min |
| 209 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 11700 | MPa | ISO 178 |
---|
IMPACT | 2) |
|
|
|
---|
Izod Impact, notched, 23°C |
| 208 | J/m | ASTM D256 |
---|
Instrumented Dart Impact Energy @ peak, 23°C |
| 13 | J | ASTM D3763 |
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 55 | kJ/m² | ISO 180/1U |
---|
Izod Impact, notched 80*10*4 +23°C |
| 27 | kJ/m² | ISO 180/1A |
---|
Multiaxial Impact |
| 13 | J | ISO 6603 |
---|
THERMAL | 2) |
|
|
|
---|
HDT, 1.82 MPa, 3.2mm, unannealed |
| 157 | °C | ASTM D648 |
---|
CTE, -40°C to 40°C, flow |
| 3.4E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 40°C, xflow |
| 4.6E-05 | 1/°C | ASTM E831 |
---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm |
| 164 | °C | ISO 75/Bf |
---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
| 159 | °C | ISO 75/Af |
---|
CTE, -40°C to 40°C, flow |
| 3.4E-05 | 1/°C | ISO 11359-2 |
---|
CTE, -40°C to 40°C, xflow |
| 4.6E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 60°C, flow |
| 3.4E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 60°C, xflow |
| 4.6E-05 | 1/°C | ISO 11359-2 |
---|
PHYSICAL | 2) |
|
|
|
---|
Density |
| 1.33 | g/cm³ | ASTM D792 |
---|
Wear Factor Washer |
| 73 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
---|
Dynamic COF |
| 0.34 | - | ASTM D3702 Modified: Manual |
---|
Static COF |
| 0.52 | - | ASTM D3702 Modified: Manual |
---|
Density |
| 1.33 | g/cm³ | ISO 1183 |
---|
INJECTION MOLDING | 3) |
|
|
|
---|
Drying Temperature |
| 80 | °C |
|
---|
Drying Time |
| 4 | Hrs |
|
---|
Melt Temperature |
| 220-250 | °C |
|
---|
Front - Zone 3 Temperature |
| 250-260 | °C |
|
---|
Middle - Zone 2 Temperature |
| 245-255 | °C |
|
---|
Rear - Zone 1 Temperature |
| 230-245 | °C |
|
---|
Mold Temperature |
| 40-65 | °C |
|
---|
Back Pressure |
| 0.2-0.3 | MPa |
|
---|
Screw Speed |
| 30-60 | rpm |
|
---|