产品详情
PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Yellow Card Link |
| E121562-102518191 | - | - |
---|
UL Recognized, 94-5VA Flame Class Rating |
| ≥1.9 | mm | UL 94 |
---|
UL Recognized, 94V-0 Flame Class Rating |
| ≥0.41 | mm | UL 94 |
---|
Oxygen Index (LOI) |
| 46 | % | ISO 4589 |
---|
MECHANICAL |
|
|
|
|
---|
Taber Abrasion, CS-17, 1 kg |
| 15 | mg/1000cy | SABIC method |
---|
Tensile Stress, break, 5 mm/min |
| 115 | MPa | ISO 527 |
---|
Tensile Strain, break, 5 mm/min |
| 4 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 4500 | MPa | ISO 527 |
---|
Flexural Stress, break, 2 mm/min |
| 185 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 4500 | MPa | ISO 178 |
---|
Ball Indentation Hardness, H358/30 |
| 140 | MPa | ISO 2039-1 |
---|
IMPACT |
|
|
|
|
---|
Izod Impact, unnotched 80*10*4 +23°C |
| 30 | kJ/m² | ISO 180/1U |
---|
Izod Impact, unnotched 80*10*4 -30°C |
| 30 | kJ/m² | ISO 180/1U |
---|
Charpy Impact, notched, 23°C |
| 7 | kJ/m² | ISO 179/2C |
---|
THERMAL |
|
|
|
|
---|
Thermal Conductivity |
| 0.24 | W/m-°C | ISO 8302 |
---|
CTE, 23°C to 150°C, flow |
| 3.0E-05 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 150°C, xflow |
| 5.1E-05 | 1/°C | ISO 11359-2 |
---|
Ball Pressure Test, 125°C +/- 2°C |
| PASSES | - | IEC 60695-10-2 |
---|
Vicat Softening Temp, Rate A/50 |
| 223 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/50 |
| 212 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/120 |
| 217 | °C | ISO 306 |
---|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
| 210 | °C | ISO 75/Be |
---|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm |
| 205 | °C | ISO 75/Ae |
---|
Relative Temp Index, Elec | 1) | 170 | °C | UL 746B |
---|
Relative Temp Index, Mech w/impact | 1) | 170 | °C | UL 746B |
---|
Relative Temp Index, Mech w/o impact | 1) | 170 | °C | UL 746B |
---|
PHYSICAL |
|
|
|
|
---|
Mold Shrinkage on Tensile Bar, flow |
| 0.4-0.6 | % | SABIC method |
---|
Density |
| 1.34 | g/cm³ | ISO 1183 |
---|
Water Absorption, (23°C/saturated) |
| 1 | % | ISO 62-1 |
---|
Moisture Absorption (23°C / 50% RH) |
| 0.6 | % | ISO 62 |
---|
Melt Volume Rate, MVR at 360°C/5.0 kg |
| 9 | cm³/10 min | ISO 1133 |
---|
ELECTRICAL |
|
|
|
|
---|
Comparative Tracking Index (UL) {PLC} |
| 4 | PLC Code | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 1 |
| ≥3 | mm | UL 746A |
---|
Hot-Wire Ignition (HWI), PLC 2 |
| ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 3 |
| ≥1.5 | mm | UL 746A |
---|
High Amp Arc Ignition (HAI), PLC 4 |
| ≥3 | mm | UL 746A |
---|
High Voltage Arc Track Rate {PLC} |
| 2 | PLC Code | UL 746A |
---|
Arc Resistance, Tungsten {PLC} |
| 6 | PLC Code | ASTM D495 |
---|
INJECTION MOLDING |
|
|
|
|
---|
Drying Temperature |
| 150 | °C |
|
---|
Drying Time |
| 4-6 | Hrs |
|
---|
Maximum Moisture Content |
| 0.02 | % |
|
---|
Melt Temperature |
| 370-410 | °C |
|
---|
Nozzle Temperature |
| 350-405 | °C |
|
---|
Front - Zone 3 Temperature |
| 360-415 | °C |
|
---|
Middle - Zone 2 Temperature |
| 350-405 | °C |
|
---|
Rear - Zone 1 Temperature |
| 340-395 | °C |
|
---|
Hopper Temperature |
| 80-120 | °C |
|
---|
Mold Temperature |
| 140-180 | °C |
|
---|
产品参数
- 否
- 中国
- PW2100
- 注塑
- ULTEM PW2100 无定形、不透明的10%玻璃纤维增强聚醚酰亚胺
- ¥128.00