PROPERTIES |
| TYPICAL VALUES | UNITS | TEST METHODS |
---|
FLAME CHARACTERISTICS | 1) |
|
|
|
---|
UL Recognized, 94HB Flame Class Rating |
| ≥1.5 | mm | UL 94 |
---|
MECHANICAL | 2) |
|
|
|
---|
Tensile Stress, yld, Type I, 50 mm/min |
| 55 | MPa | ASTM D638 |
---|
Tensile Stress, brk, Type I, 50 mm/min |
| 50 | MPa | ASTM D638 |
---|
Tensile Strain, yld, Type I, 50 mm/min |
| 5 | % | ASTM D638 |
---|
Tensile Strain, brk, Type I, 50 mm/min |
| 50 | % | ASTM D638 |
---|
Tensile Modulus, 50 mm/min |
| 2050 | MPa | ASTM D638 |
---|
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
| 80 | MPa | ASTM D790 |
---|
Flexural Modulus, 1.3 mm/min, 50 mm span |
| 2050 | MPa | ASTM D790 |
---|
Tensile Stress, yield, 50 mm/min |
| 50 | MPa | ISO 527 |
---|
Tensile Stress, break, 50 mm/min |
| 45 | MPa | ISO 527 |
---|
Tensile Strain, yield, 50 mm/min |
| 4 | % | ISO 527 |
---|
Tensile Strain, break, 50 mm/min |
| 30 | % | ISO 527 |
---|
Tensile Modulus, 1 mm/min |
| 2000 | MPa | ISO 527 |
---|
Flexural Stress, yield, 2 mm/min |
| 75 | MPa | ISO 178 |
---|
Flexural Modulus, 2 mm/min |
| 1900 | MPa | ISO 178 |
---|
IMPACT | 2) |
|
|
|
---|
Izod Impact, notched, 23°C |
| 180 | J/m | ASTM D256 |
---|
Izod Impact, notched, -30°C |
| 120 | J/m | ASTM D256 |
---|
Instrumented Dart Impact Total Energy, 23°C |
| 50 | J | ASTM D3763 |
---|
Izod Impact, notched 80*10*4 +23°C |
| 17 | kJ/m² | ISO 180/1A |
---|
Izod Impact, notched 80*10*4 -30°C |
| 10 | kJ/m² | ISO 180/1A |
---|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm |
| 18 | kJ/m² | ISO 179/1eA |
---|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm |
| 10 | kJ/m² | ISO 179/1eA |
---|
THERMAL | 2) |
|
|
|
---|
Vicat Softening Temp, Rate B/50 |
| 180 | °C | ASTM D1525 |
---|
HDT, 0.45 MPa, 3.2 mm, unannealed |
| 180 | °C | ASTM D648 |
---|
CTE, -40°C to 40°C, flow |
| 9.E-05 | 1/°C | ASTM E831 |
---|
CTE, -40°C to 40°C, xflow |
| 1.E-04 | 1/°C | ASTM E831 |
---|
CTE, 23°C to 60°C, flow |
| 1.E-04 | 1/°C | ISO 11359-2 |
---|
CTE, 23°C to 60°C, xflow |
| 9.E-05 | 1/°C | ISO 11359-2 |
---|
Ball Pressure Test, 125°C +/- 2°C |
| PASSES | - | IEC 60695-10-2 |
---|
Vicat Softening Temp, Rate A/50 |
| 230 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/50 |
| 175 | °C | ISO 306 |
---|
Vicat Softening Temp, Rate B/120 |
| 180 | °C | ISO 306 |
---|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm |
| 175 | °C | ISO 75/Be |
---|
PHYSICAL | 2) |
|
|
|
---|
Specific Gravity |
| 1.08 | - | ASTM D792 |
---|
Mold Shrinkage, flow, 3.2 mm | 4) | 1.3-1.6 | % | SABIC method |
---|
Mold Shrinkage, xflow, 3.2 mm | 4) | 1.1-1.4 | % | SABIC method |
---|
Melt Flow Rate, 280°C/5.0 kgf |
| 10 | g/10 min | ASTM D1238 |
---|
Density |
| 1.08 | g/cm³ | ISO 1183 |
---|
Water Absorption, (23°C/saturated) |
| 4.2 | % | ISO 62-1 |
---|
Moisture Absorption (23°C / 50% RH) |
| 1.2 | % | ISO 62 |
---|
Melt Volume Rate, MVR at 280°C/5.0 kg |
| 12 | cm³/10 min | ISO 1133 |
---|
ELECTRICAL | 2) |
|
|
|
---|
Volume Resistivity |
| 1.E+03-1.E+04 | Ω.cm | SABIC method |
---|
INJECTION MOLDING | 3) |
|
|
|
---|
Drying Temperature |
| 100-120 | °C |
|
---|
Drying Time |
| 2-3 | Hrs |
|
---|
Maximum Moisture Content |
| 0.07 | % |
|
---|
Melt Temperature |
| 290-320 | °C |
|
---|
Nozzle Temperature |
| 280-310 | °C |
|
---|
Front - Zone 3 Temperature |
| 290-320 | °C |
|
---|
Middle - Zone 2 Temperature |
| 280-300 | °C |
|
---|
Rear - Zone 1 Temperature |
| 260-280 | °C |
|
---|
Hopper Temperature |
| 60-80 | °C |
|
---|
Mold Temperature |
| 100-120 | °C |
|
---|