无卤阻燃TPV Santoprene 8201-70
物理性能 | -- |
| ASTMD792 | 0.948 | g/cm |
| ISO1183 | 0.950 | g/cm |
硬度 | 肖氏硬度(邵氏A,15秒,23°C,2.00mm) |
| ISO868 | 75 |
|
弹性体 | 拉伸应力-横向流量(***应变,23°C) |
| ASTMD412,ISO37 | 2.90 | MPa |
抗张强度-横向流量(断裂,23°C) |
| ASTMD412,ISO37 | 7.50 | MPa |
伸长率-横向流量(断裂,23°C) |
| ASTMD412,ISO37 | 570 | % |
23°C1 |
| ASTMD624 | 26.0 | kN/m |
23°C2 |
| ISO34-1 | 26 | kN/m |
70°C,22hr3 |
| ASTMD395B | 36 | % |
125°C,70hr4 |
| ASTMD395B | 57 | % |
70°C,22hr5 |
| ISO815 | 36 | % |
125°C,70hr6 |
| ISO815 | 57 | % |
|
|
|
|
|
|
热性能 | 脆化温度 |
| ASTMD746,ISO812 | -63.0 | °C |
RTIElec |
| UL746 | 100 | °C |
RTI | 1.10mm | UL746 | 90.0 | °C |
1.60mm | UL746 | 90.0 | °C |
3.00mm | UL746 | 95.0 | °C |
电气性能 | 相比耐漏电起痕指数(CTI) |
| UL746 | PLC0 |
|
高电弧燃烧指数(HAI) |
| UL746 | PLC0 |
|
高压电弧抗点燃指数(HVAR)(PLC) |
| UL746 | PLC5 |
|
热丝引燃(HWI) | 1.60mm | UL746 | PLC3 |
|
3.00mm | UL746 | PLC2 |
|
可燃性 | UL阻燃等级 | 1.10mm | UL94 | HB |
|
1.60mm | UL94 | HB |
|
3.00mm | UL94 | HB
|
|