Density(23°C) | 1.05 | g/cm | ISO 1183 |
Melt Volume-Flow Rate (MVR)(220°C/10.0 kg) | 9.00 | cm/10min | ISO 1133 |
Molding Shrinkage - Flow(23°C) | 0.50 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale, 23°C) | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 2200 | MPa | ISO 527-2 |
Tensile Stress(23°C) | 44.0 | MPa | ISO 527-2 |
Flexural Modulus3(23°C) | 2350 | MPa | ISO 178 |
Flexural Stress3(23°C) | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | ||
-30°C | 11 | kJ/m | |
23°C | 21 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 79.0 | °C | ISO 75-2/Af |
CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
Flame Rating(1.5 mm) | HB | UL 94 |
塑料ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一定的韧性，可在-40~100℃的温度范围内使用。塑料ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。
塑料ABS也可以说是聚苯乙烯的改性，比HIPS有较高的抗冲击强度和更好的机械强度，具有良好的加工性能，可以使用注塑机、挤出机等塑料成型设备进行注塑、挤塑、吹塑、压延、层合、发泡、热成型，还可以焊接、涂覆、电镀和机械加工。ABS的吸水性比较高，加工前需进行干燥处理，干燥温度为70~85℃，干燥时间为2~6h；ABS制品在加工中容易产生内应力，如应力太大，致使产品开裂，应进行退火处理，把制件放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。