Density | 1.04 | -- | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 1.4 | -- | % | |
Flow | 1.1 | -- | % | |
Water Absorption | *** 62 | |||
Saturation, 23°C | 1.2 | -- | % | |
Equilibrium, 23°C, 50% RH | 0.60 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Shore Hardness(Shore D, 15 sec) | 63 | 63 | *** 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 500 | 400 | MPa | *** 527-2 |
Tensile Stress(50% Strain) | 30.0 | 30.0 | MPa | *** 527-2 |
Tensile Strain(Break) | > 50 | > 50 | % | *** 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 10 | 10 | kJ/m | |
23°C | No Break | No Break | ||
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 95.0 | -- | °C | *** 75-2/B |
1.8 MPa, Unannealed | 45.0 | -- | °C | *** 75-2/A |
Continuous Use Temperature | ||||
--2 | 90.0 to 110 | -- | °C | *** 2578 |
--3 | 150 | -- | °C | Internal Method |
Melting Temperature4 | 173 | -- | °C | *** 11357-3 |
CLTE | *** 11359-2 | |||
Flow | 1.4E-4 | -- | cm/cm/°C | |
Transverse | 1.8E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+6 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+8 | 1.0E+8 | ohms·cm | IEC 60093 |
Electric Strength | 14 | 12 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | -- | 150 | V | IEC 60112 |
美国杜邦PA6 73G30L 玻璃纤维增强30%
美国杜邦PA6 73G15HSL 玻璃纤维增强15%
德国巴斯夫PA6 B30S 易流动 良好的结晶 快速成形 注射级 用于薄壁制品
德国巴斯夫PA6 B3EG3 玻璃纤维15%增强
德国巴斯夫PA6 B3EG6 玻璃纤维30%增强
德国巴斯夫PA6 B3WG6 玻璃纤维30%增强 耐热老化
德国巴斯夫PA6 B3WG3 玻璃纤维15%增强 耐热老化
德国巴斯夫PA6 B3EG10 玻璃纤维50%增强 高刚性
德国巴斯夫PA6 B3UG4 玻璃纤维20%增强 无卤无磷防火V0
德国巴斯夫PA6 C35 超韧性
在线问