无卤阻燃V0 PA6 Ultramid B3U
¥28.50
热稳定***PA6 Ultramid B3W
¥28.50
63GF增强高刚PA6 Ultramid B3WG13
¥28.50
15%玻纤热稳定PA6 Ultramid B3WG3
¥28.50
25GF增强耐热老化PA6 Ultramid B3WG5
¥28.50
巴斯夫高流动快速成型PA6 Ultramid B3S HP
B3S HP应用
典型应用包括薄壁技术零件（如外壳、配件、夹具、小零件、锚和固定夹）
Density | 1.13 | -- | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 180 | -- | cm/10min | *** 1133 |
Water Absorption | *** 62 | |||
Saturation, 23°C | 9.5 | -- | % | |
Equilibrium, 23°C, 50% RH | 3.0 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 160 | -- | MPa | *** 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 3400 | 1200 | MPa | *** 527-2 |
Tensile Stress(Yield, 23°C) | 90.0 | 45.0 | MPa | *** 527-2 |
Tensile Strain(Yield, 23°C) | 4.0 | 20 | % | *** 527-2 |
Nominal Tensile Strain at Break(23°C) | 10 | > 50 | % | *** 527-2 |
Flexural Modulus(23°C) | 3000 | -- | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | |||
-30°C | 3.0 | -- | kJ/m | |
23°C | 4.0 | 50 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179 | |||
-30°C | 200 | -- | kJ/m | |
23°C | 250kJ/m | No Break | ||
Notched Izod Impact Strength | *** 180 | |||
-30°C | 3.0 | -- | kJ/m | |
23°C | 4.0kJ/m | No Break |
在线问