巴斯夫35GF增强PA6 Ultramid B3WG7
B3WG7典型应用包括汽车离合器和加速踏板。
Density | 1.41 | -- | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 45 | -- | cm/10min | *** 1133 |
Water Absorption | *** 62 | |||
Saturation, 23°C | 6.2 | -- | % | |
Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 11000 | 7200 | MPa | *** 527-2 |
Tensile Stress(Break, 23°C) | 195 | 130 | MPa | *** 527-2 |
Tensile Strain | *** 527-2 | |||
Break, -40°C | 3.8 | -- | % | |
Break, 23°C | 3.5 | 7.0 | % | |
Flexural Modulus(23°C) | 10000 | -- | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | |||
-30°C | 13 | -- | kJ/m | |
23°C | 18 | 33 | kJ/m |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 220 | -- | °C | *** 75-2/B |
1.8 MPa, Unannealed | 215 | -- | °C | *** 75-2/A |
Melting Temperature (DSC) | 220 | -- | °C | *** 3146 |