瑞士EMS高抗冲40%GF耐热PA6 Grilon BGZ-40
Density | 1.43 | -- | g/cm | *** 1183 |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 0.50 | -- | % | |
Flow | 0.10 | -- | % | |
Water Absorption | *** 62 | |||
Saturation, 23°C | 5.0 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.5 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 220 | 120 | MPa | *** 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 11000 | 7500 | MPa | *** 527-2 |
Tensile Stress(Break) | 170 | 115 | MPa | *** 527-2 |
Tensile Strain(Break) | 3.5 | 8.0 | % | *** 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 19 | -- | kJ/m | |
23°C | 25 | 35 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | 85 | 100 | kJ/m | |
23°C | 100 | 120 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 205 | -- | °C | *** 75-2/A |
8.0 MPa, Unannealed | 120 | -- | °C | *** 75-2/C |
Continuous Use Temperature | ||||
--3 | 90.0 to 120 | -- | °C | *** 2578 |
--4 | 160 | -- | °C | Internal Method |
Melting Temperature5 | 222 | -- | °C | *** 11357-3 |
CLTE | *** 11359-2 | |||
Flow | 2.0E-5 | -- | cm/cm/°C | |
Transverse | 6.0E-5 | -- | cm/cm/°C |
PA6日常用品中的应用
PA6玻纤增强材料具有良好的尺寸稳定性及低翘曲性、焊锡性及烤漆性、易喷涂、可过超声波焊接、材料光泽度好，可染成各种鲜艳的颜色，为了满足在工业品方面的使用要求，增强PA6材料应具备以下要求：
1). 强度和耐久性，优良的刚性和耐热性的结合
2). 优化部件设计，***的着色性能，***的表面外观，能够适用于复杂的结构成型，并帮助设计***开发新造型产品
3). 良好的加工性，***的流动性及热稳定性使材料加工条件更为宽松，使注塑件微型化
4). 极高的热稳定性，能在高达270度的波峰焊锡中不挂锡
5). ***的温度和频率范围内恒定的电气性，确保装置设备的使用***百安全