安科罗40%长玻纤PA6 AKROMID B28LGF401L
Density(23°C) | 1.36 | -- | g/cm | *** 1183 |
Humidity Absorption - 62% RH(70°C) | 1.2 | -- | % | *** 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 12000 | 9500 | MPa | *** 527-2/1 |
Tensile Stress(Break) | 200 | 150 | MPa | *** 527-2/5 |
Tensile Strain(Break) | 2.5 | 2.5 | % | *** 527-2/5 |
Flexural Modulus1 | 8000 | -- | MPa | *** 178 |
Flexural Stress1 | 220 | -- | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 35 | -- | kJ/m | |
23°C | 35 | 35 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | 80 | -- | kJ/m | |
23°C | 100 | 80 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 200 | -- | °C | *** 75-2/A |
8.0 MPa, Unannealed | 190 | -- | °C | *** 75-2/C |
Melting Temperature2 | 220 | -- | °C | DIN EN 11357-1 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
Reinforcement Content | 40 | -- | % | *** 1172 |
汽车用***增强PA6复合材料制造发动机周边部件，如进气歧管、发动机罩盖等，可以代替传统金属材料，为了满足在发动机周边部件的使用要求，PA6材料应具备以下优点：
1). ***的强度和韧性，满足结构部件的机械性能
2).***耐热性，可以在高达130℃温度下连续使用
3). 长期的耐疲劳性，热老化后性能保持好
4). ***尺寸稳定性，具有防翘曲的效果
5). 表面效果好，无浮纤
6). 耐油性好，***性佳