Density(23°C) | 1.70 | -- | g/cm | ISO 1183 |
Spiral Flow2 | 35.0 | -- | cm | Internal Method |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.70 | -- | % | |
Flow | 0.30 | -- | % | |
Water Absorption(Saturation, 23°C) | 3.9 to 4.4 | -- | % | ISO 62 |
Humidity Absorption - 62% RH(70°C) | 0.90 to 1.2 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness(H 961/30) | 290 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 21000 | 13500 | MPa | ISO 527-2/1 |
Tensile Stress(Break) | 240 | 150 | MPa | ISO 527-2/5 |
Tensile Strain(Break) | 2.5 | 3.5 | % | ISO 527-2/5 |
Flexural Modulus3 | 19000 | -- | MPa | ISO 178 |
Flexural Stress3 | 370 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 19 | -- | kJ/m | |
23°C | 20 | 25 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 88 | -- | kJ/m | |
23°C | 90 | 95 | kJ/m |
日本东丽PA6 CM1030 未增强 一般用
日本东丽PA6 CM1021 中粘度 通用级
日本东丽PA6 CM1011G-30 玻璃纤维增强30% 高流动
日本东丽PA6 CM1011G-15 玻璃纤维增强15% 一般用
日本东丽PA6 CM6241M 共聚尼龙 做单丝
日本宇部PA6 1022B 中粘度
日本宇部PA6 1013B 准粘度
日本宇部PA6 1013NW8 标准粘度高速结晶
日本宇部PA6 1030B 高粘度
在线问