Density(23°C) | 1.13 | -- | g/cm | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 3200 | 1000 | MPa | ISO 527-2/1 |
Tensile Stress(Yield) | 84.0 | 43.0 | MPa | ISO 527-2/50 |
Tensile Strain | ||||
Break | 4.0 | > 15 | % | ISO 527-2/5 |
Break | > 30 | > 100 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 5.0 | 25 | kJ/m | ISO 179/1eA |
Charpy Unnotched Impact Strength(23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 60.0 | -- | °C | ISO 75-2/A |
Melting Temperature2 | 222 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Burning Rate3(1.00 mm) | <100 | -- | mm/min | FMVSS 302 |
Flame Rating | UL 94 | |||
0.8 mm | V-2 | -- | ||
1.6 mm | V-2 | -- | ||
3.2 mm | V-2 | -- |
PA6汽车领域中的应用
内外饰部件
汽车用***增强PA6复合材料具有***的耐气候性、良好的油漆性能和杰出的表现效果，为了满足在内外饰方面的使用要求，增强PA6材料应具备以下要求：
1). 高耐热，长期使用；
2）***的刚性和韧性的结合；
3). 能够满足强烈的温度和湿度的不断变化而承受巨大的应变；
4). ***尺寸稳定性，具有防翘曲的效果；
5). 具有高表面质量，表面光洁。