无卤无磷阻燃PA66 Radiflam A FR 100
Density | 1.16 | -- | g/cm | ISO 1183 |
Molding Shrinkage3 | ISO 294-4 | |||
Across Flow | 1.4 | -- | % | |
Flow | 1.4 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C, 2.00 mm | 7.7 | -- | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 1.8 | -- | % |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 3450 | 2600 | MPa | ISO 527-2/1A/1 |
Tensile Stress(Yield) | 77.0 | 50.0 | MPa | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | 12 | > 50 | % | ISO 527-2/1A/50 |
Flexural Modulus4 | 3200 | -- | MPa | ISO 178 |
Flexural Stress4 | 115 | -- | MPa | ISO 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 4.0 | -- | kJ/m | |
23°C | 4.5 | 6.5 | kJ/m |
Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/Af |
Vicat Softening Temperature | 220 | -- | °C | ISO 306/B50 |
Melting Temperature5 | 260 | -- | °C | ISO 11357-3 |
Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity6 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity6 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 600 | -- | V | IEC 60112 |
Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
0.40 mm | V-0 | -- | ||
0.8 mm | V-0 | -- |
PA66美国首诺21SPC高刚性 耐化学性
PA66美国首诺R513H R533H玻纤增强,高强度,特殊热稳定,耐水解。通过FDA、UL认证。通过GM、Ford、Chryster、Delphi、Valeo
等汽车认证,适用于汽车零部件。机械部件等。
PA66德国巴斯夫A3X2G5 A3X2G7玻纤增强,红磷阻燃剂长期稳定性,具有***的机械性能。
PA66塑胶原料德国巴斯夫A3EG6 A3HG5 A3EG7 A3WG6玻纤增强用于需要高刚性和尺寸稳定性的机械部件护罩。
PA66德国巴斯夫C3U高韧性 无卤素和磷阻燃级 。
PA66德国巴斯夫A3K高流动性,用于高应力工程制件如轴承,齿轮及连接器,插座。
PA66美国杜邦101F特殊级适合耐热性好的制品。
PA66塑胶原料美国杜邦101L高强度注塑级 改进机器进料和脱模特性。