经销朗盛PA6 Durethan BCF30XH2.0玻纤碳纤增强
Density(23°C) | 1.33 | -- | g/cm | ISO 1183 |
Melt Volume-Flow Rate (MVR)(260°C/5.0 kg) | 15 | -- | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 13500 | 6700 | MPa | ISO 527-2/1 |
Tensile Stress(Break, 23°C) | 195 | 100 | MPa | ISO 527-2/5 |
Tensile Strain(Break, 23°C) | 3.1 | 5.0 | % | ISO 527-2/5 |
Flexural Modulus7(23°C) | 11500 | 6800 | MPa | ISO 178/A |
Flexural Stress7 | ISO 178/A | |||
23°C | 280 | 160 | MPa | |
3.5% Strain, 23°C | -- | 145 | MPa | |
Flexural Strain at Flexural Strength8(23°C) | 3.5 | 5.0 | % | ISO 178/A |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | <10 | -- | kJ/m | |
23°C | 11 | -- | kJ/m |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 219 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 140 | -- | °C | ISO 75-2/C |
Vicat Softening Temperature | 214 | -- | °C | ISO 306/B120 |
Melting Temperature9 | 220 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
Transverse : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | 4.0E+4 | -- | ohms | IEC 60093 |
Volume Resistivity(23°C) | 2.0E+5 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flame Rating | UL 94 | |||
0.75 mm | HB | -- | ||
1.5 mm | HB | -- |