SCHULATEC PA6 HC 7150导热高刚PA6
Density | 1.80 | g/cm | ISO 1183/A |
Viscosity Number | 125 | cm/g | ISO 307 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 12500 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Break) | 120 | MPa | ISO 527-2/1A/5 |
Tensile Strain(Break) | 1.9 | % | ISO 527-2/1A/5 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 3.5 | kJ/m | |
23°C | 5.0 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | 24 | kJ/m | |
23°C | 30 | kJ/m |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 215 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 200 | °C | ISO 75-2/Af |
Thermal Conductivity | 1.2 | W/m/K | ISO 8302 |
Flammability | Nominal Value | Unit | Test Method |
Burning Rate | |||
2.00 mm | <100 | mm/min | ISO 3795 |
2.00 mm | <100 | mm/min | FMVSS 302 |