30%滑石填充PA6 SCHULAMID 6 MT 30
¥35.00
无卤阻燃PA6 SCHULAMID 6 NV 12 FR
Density | 1.15 | -- | g/cm | ISO 1183/A |
Viscosity Number | 130 | -- | cm/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 3400 | 1400 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Yield) | 70.0 | 40.0 | MPa | ISO 527-2/1A/50 |
Tensile Strain(Yield) | 4.0 | 15 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 3.5 | 5.0 | kJ/m | |
23°C | 4.0 | 15 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | No Break | No Break | ||
23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/Af |
Vicat Softening Temperature | ||||
-- | 203 | -- | °C | ISO 306/B50 |
-- | 218 | -- | °C | ISO 306/A50 |
Ball Pressure Test(200°C) | Pass | -- | IEC 60695-10-2 |
Flame Rating | UL 94,IEC 60695-11-10, -20 | |||
0.38 mm | V-0 | -- | ||
0.75 mm | V-0 | -- | ||
1.5 mm | V-0 | -- | ||
3.0 mm | V-0 | -- |