SCHULAMID 6 GF 30 HI高抗冲30%GF/PA6
Density | 1.31 | -- | g/cm | ISO 1183/A |
Water Absorption(Equilibrium, 23°C, 50% RH) | 1.9 | -- | % | ISO 62 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 8300 | 5000 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Break) | 135 | 85.0 | MPa | ISO 527-2/1A/5 |
Tensile Strain(Break) | 4.0 | 9.0 | % | ISO 527-2/1A/5 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 12 | -- | kJ/m | |
23°C | 18 | 30 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 78 | -- | kJ/m | |
23°C | 85 | 95 | kJ/m |
Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Af |
Vicat Softening Temperature | ||||
-- | 205 | -- | °C | ISO 306/B50 |
-- | 220 | -- | °C | ISO 306/A50 |
Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | > 1.0E+15 | -- | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+13 | -- | ohms·m | IEC 62631-3-1 |
Comparative Tracking Index | 550 | -- | V | IEC 60112 |