30%GF热稳定PA6 SCHULAMID 6 GF 30 H
Density | 1.35 | -- | g/cm | ISO 1183/A |
Water Absorption(Equilibrium, 23°C, 50% RH) | 2.0 | -- | % | ISO 62 |
Viscosity Number | 145 | -- | cm/g | ISO 307 |
Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness(H 358/30) | 200 | -- | MPa | ISO 2039-1 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 9500 | 5000 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Break) | 170 | 100 | MPa | ISO 527-2/1A/5 |
Tensile Strain(Break) | 3.5 | 8.0 | % | ISO 527-2/1A/5 |
Flexural Modulus | 7800 | -- | MPa | ISO 178 |
Flexural Stress | 210 | -- | MPa | ISO 178 |
Flexural Strain at Flexural Strength | 3.7 | -- | % | ISO 178 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 9.0 | -- | kJ/m | |
23°C | 12 | 30 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 60 | -- | kJ/m | |
23°C | 80kJ/m | No Break |
Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/Af |
Vicat Softening Temperature | ||||
-- | 210 | -- | °C | ISO 306/B50 |
-- | 217 | -- | °C | ISO 306/A50 |