SCHULAMID 6 GF 30 GID LS抗紫外线30%玻纤PA6
Density | 1.35 | -- | g/cm | ISO 1183/A |
Viscosity Number | 145 | -- | cm/g | ISO 307 |
Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 8800 | 5200 | MPa | ISO 527-1/1A/1 |
Tensile Stress(Break) | 155 | 90.0 | MPa | ISO 527-2/1A/5 |
Tensile Strain(Break) | 3.5 | 8.5 | % | ISO 527-2/1A/5 |
Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 8.0 | -- | kJ/m | |
23°C | 12 | 26 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 74 | -- | kJ/m | |
23°C | 80 | 95 | kJ/m |
Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 195 | -- | °C | ISO 75-2/Af |
Flammability | Dry | Conditioned | Unit | Test Method |
Burning Rate | ||||
2.00 mm | <100 | -- | mm/min | ISO 3795 |
2.00 mm | <100 | -- | mm/min | FMVSS 302 |