40%矿物填充PA66 TECHNYL A31T1MZ40索尔维
|
|
|
|
Density | 1.67g/cc | 0.0603lb/in | *** 1183/A |
Water Absorption | 0.43 % @Temperature 23.0 °C, Time 86400 sec | 0.43 % @Temperature 73.4 °F, Time 24.0 hour | *** 62 |
|
Mechanical Properties | Metric | English | Comments |
---|
Tensile Strength at Break | 77.0MPa | 11200psi | *** 527 Type 1A |
Elongation at Break | 1.7 % | 1.7 % | *** 527 Type 1A |
Tensile Modulus | 6.90GPa | 1000ksi | *** 527 Type 1A |
Charpy Impact Unnotched | 2.50J/cm | 11.9ft-lb/in | *** 179/1eU |
Charpy Impact, Notched | 0.220J/cm | 1.05ft-lb/in | *** 179/1eA |
|
Electrical Properties | Metric | English | Comments |
---|
Dielectric Strength | 30.0kV/mm | 762kV/in | IEC 60243 |
Comparative Tracking Index | 400V | 400V | Solution A; IEC 60112 |
|
Thermal Properties | Metric | English | Comments |
---|
Melting Point | 263°C | 505°F | *** 11357 |
Deflection Temperature at 1.8 MPa (264 psi) | 120°C | 248°F | *** 75/Af |
Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | 1210 |
Oxygen Index | 46.5 % | 46.5 % | *** 4589 |
Glow Wire Flammability Index | 960°C @Thickness 0.800 mm | 1760°F @Thickness 0.0315 in | *** 60695-2-12 |
| 960°C @Thickness 1.60 mm | 1760°F @Thickness 0.0630 in | *** 60695-2-12 |
| 960°C @Thickness 3.20 mm | 1760°F @Thickness 0.126 in | *** 60695-2-12 |
|
Processing Properties | Metric | English | Comments |
---|
Feed Temperature | 270-275°C | 518-527°F |
|
Front Barrel Temperature | 285-290°C | 545-554°F |
|
Mold Temperature | 60.0-80.0°C | 140-176°F |
|
Drying Temperature | 80.0°C | 176°F |
|
Moisture Content | <= 0.20 % | <=>
|
|
PA66优点
1、具高抗张强度;2、耐韧、耐冲击性特优;3、自润性、***性佳;4、低温特性佳;5、具自熄性;
PA66用途
***应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些***工程制品。
电子电器:连接器、卷线轴、计时器、护盖断路器、开关壳座
汽车: 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座
工业零件:椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输