Density | 1.37 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR) | 25 | cm/10min | *** 1133 |
Water Absorption | *** 62 | ||
Saturation, 23°C | 5.5 | % | |
Equilibrium, 23°C, 50% RH | 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 10100 | MPa | *** 527-2 |
Tensile Stress(Break, 23°C) | 188 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 3.3 | % | *** 527-2 |
Flexural Modulus(23°C) | 8850 | MPa | *** 178 |
Flexural Stress(23°C) | 275 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | ||
-30°C | 9.0 | kJ/m | |
23°C | 11 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179 | ||
-30°C | 63 | kJ/m | |
23°C | 77 | kJ/m | |
Notched Izod Impact Strength | *** 180 | ||
-40°C | 8.3 | kJ/m | |
23°C | 11 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 249 | °C | *** 75-2/A |
Melting Temperature (DSC) | 260 | °C | *** 3146 |