SCHULAMID 66 GF30 FR2 H2无卤阻燃30%GF增强PA66
Density | 1.44 | g/cm | ISO 1183/A |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 11500 | MPa | ISO 527-1/1A |
Tensile Stress(Break) | 140 | MPa | ISO 527-2/1A |
Tensile Strain(Break) | 2.4 | % | ISO 527-2/1A |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 10 | kJ/m | ISO 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 65 | kJ/m | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 256 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed | 242 | °C | ISO 75-2/Af |
Vicat Softening Temperature | |||
-- | 229 | °C | ISO 306/B50 |
-- | 255 | °C | ISO 306/A50 |
Electrical | Nominal Value | Unit | Test Method |
Comparative Tracking Index | 600 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
Burning Rate | ISO 3795 | ||
0.750 mm, Self-Extinguishing | 0.0 | mm/min | |
1.50 mm, Self-Extinguishing | 0.0 | mm/min | |
3.00 mm, Self-Extinguishing | 0.0 | mm/min | |
Flammability Classification | IEC 60695-11-10, -20 | ||
0.75 mm | V-0 | ||
1.5 mm | V-0 | ||
3.0 mm | V-0 |