普立万15%玻璃珠PA66 Bergamid A65 GK15
Density 2 (23°C) | 1.23 | g/cm³ | DIN 53479 |
Molding Shrinkage 3 (23°C, 4.00 mm) | 1.4 to 1.9 | % | ISO 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 4 (23°C, 4.00 mm, Injection Molded) | 4100 | MPa | ISO 527-1/1 |
Tensile Stress 4 (Break, 23°C, 4.00 mm, Injection Molded) | 60.0 | MPa | ISO 527-2/5 |
Tensile Strain 4 (Break, 23°C, 4.00 mm, Injection Molded) | 1.5 | % | ISO 527-2/5 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | |||
-30°C, Injection Molded | 1.4 | kJ/m² | ISO 179 |
23°C 4 | 2.5 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength | |||
-30°C, Injection Molded | 15 | kJ/m² | ISO 179 |
23°C, Injection Molded 4 | 15 | kJ/m² | ISO 179/1eA |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 224 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 75.5 | °C | ISO 75-2/A |
Maximum Use Temperature | |||
long term (GTP 50% tensile) | 85 | °C | IEC 216 |
short time | 180 | °C | IEC 60216 |
Melting Temperature (DSC) | 261 | °C | ISO 3146 |