美国SABIC抗紫外线阻燃PC LEXAN 925U
Lexan* 925U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing additional weathering capability. Lexan 925U resin is available in various opaque color options and is a general-purpose resin that is an excellent candidate for a wide variety of applications.
| 添加剂 | |
| 特性 | Chlorine Free 抗紫外线性能良好 通用 无溴 阻燃性
|
| 用途 | |
| 比重 | 1.19 | g/cm | ASTM D792 |
| 熔流率（熔体流动速率）(300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| 收缩率 - 流动(3.20 mm) | 0.60 到 0.80 | % | 内部方法 |
| 室外适用性 | f1 |
| UL 746C |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸模量1 | 2270 | MPa | ASTM D638 |
| 抗张强度2 |
|
| ASTM D638 |
| 屈服 | 62.0 | MPa | ASTM D638 |
| 断裂 | 65.0 | MPa | ASTM D638 |
| 伸长率3 |
|
| ASTM D638 |
| 屈服 | 6.0 | % | ASTM D638 |
| 断裂 | 130 | % | ASTM D638 |
| 弯曲模量4(50.0 mm 跨距) | 2340 | MPa | ASTM D790 |
| 弯曲强度5(屈服, 50.0 mm 跨距) | 101 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度(23°C) | 800 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击(23°C, Total Energy) | 73.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
| ASTM D648 |
| 0.45 MPa, 未退火, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 126 | °C | ASTM D648 |
| 维卡软化温度 | 143 | °C | ASTM D15256 |
PC是一种非晶体工程材料，具有特别好的抗冲击强度、热稳定性、光泽度、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口伊估德冲击强度（otched Izod impact stregth）非常高，并且收缩率很低，一般为0.1%~0.2%。