批发科思创高流动PC APEC 1795***173度
Density(23°C) | 1.17 | g/cm | ISO 1183 |
Melt Mass-Flow Rate (MFR)(330°C/2.16 kg) | 31 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(330°C/2.16 kg) | 30 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2400 | MPa | ISO 527-2/1 |
Tensile Stress(Yield, 23°C) | 71.0 | MPa | ISO 527-2/50 |
Tensile Strain(Yield, 23°C) | 6.6 | % | ISO 527-2/50 |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Flexural Modulus4(23°C) | 2400 | MPa | ISO 178 |
Flexural Stress4(23°C) | 105 | MPa | ISO 178 |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 148 | °C | ISO 75-2/A |
Vicat Softening Temperature | 173 | °C | ISO 306/B120 |
Flame Rating(1.5 mm) | HB | UL 94 | |
Glow Wire Flammability Index | 850 | °C | IEC 60695-2-12 |
Oxygen Index5 | 26 | % | ISO 4589-2 |