产品详情
导电PC LATISTAT 87/28-06
Density | 1.22 | g/cm | ISO 1183 |
Molding Shrinkage2 | ISO 294-4 | ||
Across Flow : 2.00 mm | 0.70 to 0.90 | % | |
Flow : 2.00 mm | 0.70 to 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 2620 | MPa | ISO 527-1/1 |
Tensile Stress | ISO 527-2/5 | ||
Yield, 23°C | 55.2 | MPa | |
Break, 23°C | 49.6 | MPa | |
Tensile Strain | ISO 527-2/5 | ||
Yield, 23°C | 4.5 | % | |
Break, 23°C | 6.0 | % | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 20 | kJ/m | ISO 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 93 | kJ/m | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
Continuous Use Temperature3 | 120 | °C | ASTM E1641/E1877 |
Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
为您推荐
-
-
-
SCHULAMID 66 MV HI增韧抗冲PA66 ¥48.00
-
-
-
SCHULAMID 66 MV 5 FR无卤阻燃PA66 ¥55.00
在线问
产品参数
- LATISTAT
- 否
- 意大利
- LATI
- 87/28-06
- 品牌经销
- 标准料
- PC
- 注塑级
- 导电级
- 25KG/包
- 导电PC