10%GB/15%PTFE耐磨PC LUBRICOMP DBL32美国SABIC
Density / Specific Gravity | 1.37 | g/cm³ | ASTM D792, *** 1183 |
Molding Shrinkage | |||
Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
Across Flow : 24 hr | 0.96 | % | *** 294-4 |
Flow : 24 hr | 0.80 | % | *** 294-4 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 1 | 2060 | MPa | ASTM D638 |
-- | 2580 | MPa | *** 527-1/1 |
Tensile Strength | |||
Yield 2 | 42.0 | MPa | ASTM D638 |
Yield | 43.0 | MPa | *** 527-2/5 |
Break 2 | 38.0 | MPa | ASTM D638 |
Break | 38.0 | MPa | *** 527-2/5 |
Tensile Elongation | |||
Yield 2 | 5.4 | % | ASTM D638 |
Yield | 5.1 | % | *** 527-2/5 |
Break 2 | 22 | % | ASTM D638 |
Break | 18 | % | *** 527-2/5 |
Flexural Modulus | |||
50.0 mm Span 3 | 2750 | MPa | ASTM D790 |
-- 4 | 2400 | MPa | *** 178 |
Flexural Stress | 69.0 | MPa | *** 178 |
Coefficient of Friction 5 | ASTM D3702 | ||
Dynamic | 0.41 | ||
Static | 0.48 | ||
Wear Factor 5 | 280 | 10^-8 mm³/N·m | ASTM D3702 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact | |||
23°C | 190 | J/m | ASTM D256 |
23°C 6 | 14 | kJ/m² | *** 180/1A |