抗紫外线增强阻燃EMERGE PC 8731-13盛禧奥
Density / Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
Molding Shrinkage | ASTM D955 | ||
Flow | 0.35 to 0.50 | % | |
Across Flow | 0.40 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus 3 | 4000 | MPa | ASTM D638 |
Tensile Strength 4 (Break) | 65.0 | MPa | ASTM D638 |
Tensile Elongation 5 (Break) | 4.0 | % | ASTM D638 |
Flexural Modulus | 3800 | MPa | ASTM D790 |
Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed | 138 | °C | |
1.8 MPa, Unannealed | 129 | °C | |
1.8 MPa, Annealed | 139 | °C | |
Ball Indentation Temperature | > 130 | °C | IEC 60598-1 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
Volume Resistivity (2.00 mm) | 1.0E+16 | ohms·cm | IEC 60093 |
Electric Strength (2.00 mm) | 70 | kV/mm | IEC 60243-1 |
Dissipation Factor 6 | IEC 60250 | ||
2.00 mm, 50 Hz | 8.0E-3 | ||
2.00 mm, 1 MHz | 0.016 | ||
Comparative Tracking Index (3.00 mm, Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating 6 | UL 94 | ||
1.5 mm | V-0 | ||
3.0 mm | 5VA | ||
Glow Wire Flammability Index 6 (2.0 mm) | 960 | °C | IEC 60695-2-12 |