PC/PBT 5220U 抗冲击性,耐候抗紫外线
XENOY™ 5220U resin
Polycarbonate + PBT
SABIC Innovative Plastics
产品说明:
Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance.
物性信息:
基本信息 |
|
---|
黄卡编号 | |
添加剂 | |
特性 | |
加工方法 | |
多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Compressive Stress vs. Strain (ASTM D695) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
物理性能 | 额定值 | 单位制 | 测试方法 |
---|
比重 |
|
|
|
-- | 1.21 | g/cm³ | ASTM D792 |
-- | 1.22 | g/cm³ | ISO 1183 |
特定体积 | 0.830 | cm³/g | ASTM D792 |
熔流率(熔体流动速率) (250°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (250°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
收缩率 |
|
| 内部方法 |
流动 : 3.20 mm | 0.80 到 1.0 | % | 内部方法 |
横向流动 1 | 0.80 到 1.0 | % | 内部方法 |
吸水率 |
|
| ISO 62 |
饱和, 23°C | 0.50 | % | ISO 62 |
平衡, 23°C, 50% RH | 0.15 | % | ISO 62 |
室外适用性 | f2 |
| UL 746C |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|
拉伸模量 |
|
|
|
-- 2 | 2250 | MPa | ASTM D638 |
-- 3 | 2250 | MPa | ASTM D638 |
-- | 2050 | MPa | ISO 527-2/1 |
抗张强度 |
|
|
|
屈服 4 | 53.0 | MPa | ASTM D638 |
屈服 | 50.0 | MPa | ISO 527-2/50 |
断裂 5 | 51.0 | MPa | ASTM D638 |
断裂 | 50.0 | MPa | ISO 527-2/50 |
伸长率 |
|
|
|
屈服 6 | 4.0 | % | ASTM D638 |
屈服 | 4.0 | % | ISO 527-2/50 |
断裂 7 | 120 | % | ASTM D638 |
断裂 | 120 | % | ISO 527-2/50 |
弯曲模量 |
|
|
|
50.0 mm 跨距 8 | 2030 | MPa | ASTM D790 |
-- 9 | 2000 | MPa | ISO 178 |
弯曲应力 |
|
|
|
-- | 80.0 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 10 | 84.0 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|
简支梁缺口冲击强度 11(23°C) | 55 | kJ/m² | ISO 179/1eA |
悬壁梁缺口冲击强度 |
|
|
|
-40°C | 300 | J/m | ASTM D256 |
-30°C | 530 | J/m | ASTM D256 |
23°C | 710 | J/m | ASTM D256 |
-30°C 12 | 30 | kJ/m² | ISO 180/1A |
23°C 13 | 50 | kJ/m² | ISO 180/1A |
装有测量仪表的落镖冲击 (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|
载荷下热变形温度 |
|
|
|
0.45 MPa, 未退火, 6.40 mm | 107 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 84.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 6.40 mm | 99.0 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 14 | 75.0 | °C | ISO 75-2/Af |
维卡软化温度 |
|
|
|
-- | 122 | °C | ASTM D1525 15 |
-- | 120 | °C | ISO 306/B50 |
-- | 125 | °C | ISO 306/B120 |
线形热膨胀系数 |
|
| ASTM E831, ISO 11359-2 |
流动 : -40 到 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
横向 : -40 到 40°C | 9.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
RTI Elec | 75.0 | °C | UL 746 |
RTI Imp | 75.0 | °C | UL 746 |
RTI | 75.0 | °C | UL 746 |
电气性能 | 额定值 |
| 测试方法 |
---|
耐电弧性 16 | PLC 5 |
| ASTM D495 |
相比耐漏电起痕指数(CTI) | PLC 1 |
| UL 746 |
高电弧燃烧指数(HAI) | PLC 0 |
| UL 746 |
高电压电弧起痕速率 (HVTR) | PLC 0 |
| UL 746 |
热丝引燃 (HWI) | PLC 3 |
| UL 746 |
可燃性 | 额定值 |
| 测试方法 |
---|
UL 阻燃等级 (1.50 mm) | HB |
| UL 94 |
注射 | 额定值 | 单位制 |
|
---|
干燥温度 | 110 | °C |
|
干燥时间 | 4.0 到 6.0 | hr |
|
干燥时间, | 8.0 | hr |
|
建议的水分含量 | 0.020 | % |
|
建议注射量 | 50 到 80 | % |
|
料筒后部温度 | 243 到 266 | °C |
|
料筒中部温度 | 249 到 271 | °C |
|
料筒前部温度 | 254 到 277 | °C |
|
射嘴温度 | 254 到 271 | °C |
|
加工(熔体)温度 | 260 到 277 | °C |
|
模具温度 | 65.6 到 87.8 | °C |
|
背压 | 0.345 到 0.689 | MPa |
|
螺杆转速 | 50 到 80 | rpm |
|
排气孔深度 | 0.013 到 0.020 | mm |
|
挤出 | 额定值 | 单位制 |
|
---|
干燥温度 | 110 到 116 | °C |
|
干燥时间 | 4.0 到 6.0 | hr |
|
建议的水分含量 | 1.0E-3 到 0.020 | % |
|
料筒1区温度 | 171 到 204 | °C |
|
料筒2区温度 | 193 到 254 | °C |
|
料筒3区温度 | 204 到 282 | °C |
|
料筒4区温度 | 204 到 282 | °C |
|
接头温度 | 227 到 282 | °C |
|
熔体温度 | 243 到 277 | °C |
|
口模温度 | 232 到 282 | °C |
|