代理沙伯基础创新低粘度PC/ABS Cycoloy C1950
| 比重 | 1.12 g/cc | 1.12 g/cc | ASTM D 792 |
| 吸水率 | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D 570 |
| 平衡吸湿 | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | ASTM D 570 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C | 7.0 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D 1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 |
| 伸长率 (断裂) | 80 % | 80 % | Type I, 50 mm/min; ASTM D 638 |
| 屈服伸长率 | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D 638 |
| 拉伸模量 | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D 638 |
| 弯曲强度 | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 弯曲模量 | 2.48 GPa | 360 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 悬壁梁缺口冲击强度 | 1.06 J/cm @Temperature -30.0 °C | 1.99 ft-lb/in @Temperature -22.0 °F | ASTM D 256 |
| 5.34 J/cm @Temperature 23.0 °C | 10.0 ft-lb/in @Temperature 73.4 °F | ASTM D 256 | |
| 冲击试验 | 40.0 J @Temperature -30.0 °C | 29.5 ft-lb @Temperature -22.0 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| 54.0 J @Temperature 23.0 °C | 39.8 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |