经销沙伯基础***阻燃高流动PC/ABS CYCOLOY C2950HF
Density / Specific Gravity | 1.18 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR)(260°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
Flow : 3.20 mm | 0.40 to 0.60 | % | |
Water Absorption | ASTM D570 | ||
24 hr, 23°C | 0.10 | % | |
Saturation, 23°C | 0.40 | % | |
Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 121 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength2(Yield) | 64.0 | MPa | ASTM D638 |
Tensile Elongation2 | ASTM D638 | ||
Yield | 5.0 | % | |
Break | 40 | % | |
Flexural Modulus3(100 mm Span) | 2580 | MPa | ASTM D790 |
Flexural Strength3(Yield, 100 mm Span) | 96.0 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact(23°C) | 450 | J/m | ASTM D256 |
Instrumented Dart Impact(23°C, Energy at Peak) | 54.0 | J | ASTM D3763 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | ASTM D648 | ||
0.45 MPa, Unannealed, 6.40 mm | 101 | °C | |
1.8 MPa, Unannealed, 3.20 mm | 87.0 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 95.0 | °C |
Flame Rating | UL 94 | ||
0.76 mm | V-2 | ||
1.5 mm | V-0 | ||
2.5 mm | 5VB | ||
3.4 mm | 5VA |