Density / Specific Gravity | 1.10 | g/cm³ | ASTM D792, *** 1183 |
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 14 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (265°C/5.0 kg) | 20 | cm³/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
Flow : 3.20 mm | 0.50 to 0.80 | % | |
Water Absorption (24 hr, 23°C) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 2 | 2130 | MPa | ASTM D638 |
-- | 2200 | MPa | *** 527-1/1 |
Tensile Strength | |||
Yield 3 | 50.0 | MPa | ASTM D638 |
Yield | 45.0 | MPa | *** 527-2/50 |
Break 3 | 44.0 | MPa | ASTM D638 |
Tensile Elongation 3 | ASTM D638 | ||
Yield | 8.6 | % | |
Break | 150 | % | |
Flexural Modulus | |||
50.0 mm Span 4 | 2100 | MPa | ASTM D790 |
-- 5 | 2000 | MPa | *** 178 |
Flexural Strength 4 (Yield, 50.0 mm Span) | 72.0 | MPa | ASTM D790 |
Poisson&＃39;s Ratio | 0.35 | *** 527-2 | |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 6 | *** 179/1eA | ||
-30°C | 35 | kJ/m² | |
23°C | 50 | kJ/m² | |
Notched Izod Impact | |||
-30°C | 430 | J/m | ASTM D256 |
23°C | 530 | J/m | ASTM D256 |
-40°C 7 | 41 | kJ/m² | *** 180/1A |
-30°C 7 | 41 | kJ/m² | *** 180/1A |
23°C 7 | 46 | kJ/m² | *** 180/1A |
Instrumented Dart Impact | ASTM D3763 | ||
-30°C, Total Energy | 33.0 | J | |
23°C, Total Energy | 41.0 | J |