Physical Properties	Metric	English	Comments

Specific Gravity	1.51 g/cc	1.51 g/cc	ASTM D792
Density	1.51 g/cc	0.0546 lb/in³	*** 1183
Moisture Absorption	0.0200 %	0.0200 %	Injection Molding
	0.500 %	0.500 %	23°C / 50% RH; *** 62
Water Absorption at Saturation	0.90 %	0.90 %	*** 62-1
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm @Thickness 3.20 mm	0.0020 - 0.0040 in/in @Thickness 0.126 in	SABIC method
Melt Flow	5.0 g/10 min @Load 6.60 kg, Temperature 337 °C	5.0 g/10 min @Load 14.6 lb, Temperature 639 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	158 MPa	22900 psi	5 mm/min; ASTM D638
	165 MPa	23900 psi	5 mm/min; *** 527
Tensile Strength, Yield	165 MPa	23900 psi	5 mm/min; *** 527
	168 MPa	24400 psi	5 mm/min; ASTM D638
Elongation at Break	2.0 %	2.0 %	5 mm/min; *** 527
	3.0 %	3.0 %	5 mm/min; ASTM D638
Elongation at Yield	2.0 %	2.0 %	5 mm/min; *** 527
	3.0 %	3.0 %	5 mm/min; ASTM D638
Tensile Modulus	9.30 GPa	1350 ksi	5 mm/min; ASTM D638
	9.50 GPa	1380 ksi	1 mm/min; *** 527
Flexural Strength	220 MPa	31900 psi	yld, 1.3 mm/min, 50 mm span; ASTM D790
	225 MPa	32600 psi	yield, 2 mm/min; *** 178
Flexural Modulus	8.50 GPa	1230 ksi	2 mm/min; *** 178
	9.25 GPa	1340 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact Notched	85.0 J	62.7 ft-lb	ASTM D256
	90.0 J @Temperature -30.0 °C	66.4 ft-lb @Temperature -22.0 °F	ASTM D256
Izod Impact, Unnotched	4.27 J/cm	8.00 ft-lb/in	ASTM D4812
Izod Impact, Notched (***)	10.0 kJ/m²	4.76 ft-lb/in²	80104; *** 180/1A
	10.0 kJ/m² @Temperature -30.0 °C	4.76 ft-lb/in² @Temperature -22.0 °F	80104; *** 180/1A
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	Edgew 80104 sp=62mm; *** 179/1eA
Dart Drop, Total Energy	10.0 J	7.38 ft-lb	ASTM D3763

Electrical Properties	Metric	English	Comments
Arc Resistance	60 - 120 sec	60 - 120 sec	ASTM D495
Comparative Tracking Index	100 - 175 V	100 - 175 V	UL 746A
Hot Wire Ignition, HWI	15 - 30 sec @Thickness >=1.50 mm	15 - 30 sec @Thickness >=0.0591 in	UL 746A
	60 - 120 sec @Thickness >=3.00 mm	60 - 120 sec @Thickness >=0.118 in	UL 746A
High Amp Arc Ignition, HAI	0.00 - 15 arcs @Thickness >=3.00 mm	0.00 - 15 arcs @Thickness >=0.118 in	UL 746A
	15 - 30 arcs @Thickness >=1.50 mm	15 - 30 arcs @Thickness >=0.0591 in	UL 746A
High Voltage Arc-Tracking Rate, HVTR	80.0 - 150 mm/min	3.15 - 5.91 in/min	UL 746A

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	16.0 µm/m-°C @Temperature -40.0 - 40.0 °C	8.89 µin/in-°F @Temperature -40.0 - 104 °F	*** 11359-2
	19.8 µm/m-°C @Temperature -20.0 - 150 °C	11.0 µin/in-°F @Temperature -4.00 - 302 °F	ASTM E831
CTE, linear, Transverse to Flow	16.0 µm/m-°C @Temperature -40.0 - 40.0 °C	8.89 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E831
	41.0 µm/m-°C @Temperature -40.0 - 40.0 °C	22.8 µin/in-°F @Temperature -40.0 - 104 °F	*** 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F	Flatw 80104 sp=64mm; *** 75/Af
	210 °C @Thickness 6.40 mm	410 °F @Thickness 0.252 in	unannealed; ASTM D648
Vicat Softening Point	213 °C	415 °F	Rate B/50; *** 306
	220 °C	428 °F	Rate B/120; *** 306
	227 °C	441 °F	Rate B/50; ASTM D1525
UL RTI, Electrical	180 °C	356 °F	UL 746B
UL RTI, Mechanical with Impact	170 °C	338 °F	UL 746B
UL RTI, Mechanical without Impact	180 °C	356 °F	UL 746B
Flammability, UL94	V-0 @Thickness >=0.250 mm	V-0 @Thickness >=0.00984 in	UL 94
	5VA @Thickness >=1.20 mm	5VA @Thickness >=0.0472 in	UL 94
Glow Wire Ignition Temperature	900 °C @Thickness 2.00 mm	1650 °F @Thickness 0.0787 in	IEC 60695-2-13
Glow Wire Flammability Index	960 °C @Thickness 2.00 mm	1760 °F @Thickness 0.0787 in	IEC 60695-2-12

Processing Properties	Metric	English	Comments
Nozzle Temperature	345 - 400 °C	653 - 752 °F
Zone 2	340 - 400 °C	644 - 752 °F
Zone 3	345 - 400 °C	653 - 752 °F
Melt Temperature	350 - 400 °C	662 - 752 °F	Injection Molding
Mold Temperature	135 - 165 °C	275 - 329 °F
Drying Temperature	150 °C	302 °F	Injection Molding
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour	Injection Molding
	24.0 hour	24.0 hour	Cumulative; Injection Molding
Back Pressure	0.300 - 0.700 MPa	43.5 - 102 psi
Shot Size	40 - 60 %	40 - 60 %
Vent Depth	0.00250 - 0.00760 cm	0.000984 - 0.00299 in
Screw Speed	40 - 70 rpm	40 - 70 rpm