Density / Specific Gravity | 1.02 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR)(230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
Molding Shrinkage - Flow(3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Strength2(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
Tensile Elongation2(Break, 3.20 mm) | <10 | % | ASTM D638 |
Flexural Modulus3(6.40 mm) | 2750 | MPa | ASTM D790 |
Flexural Strength3(6.40 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact(23°C, 3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed, 6.40 mm) | 145 | °C | ASTM D648 |