Density | 0.905 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
Molding Shrinkage (24 hr) | 1.6 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 1300 | MPa | ISO 527-1/1A/1 |
Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/1A |
Tensile Strain (Yield) | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-20°C | 5.0 | kJ/m² | |
0°C | 8.0 | kJ/m² | |
23°C | 13 | kJ/m² | |
Notched Izod Impact Strength | ISO 180/1A | ||
-20°C | 5.0 | kJ/m² | |
0°C | 7.0 | kJ/m² | |
23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load 2 | |||
0.45 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed, 4.00 mm | 55.0 | °C | ISO 75-2/Af |
Vicat Softening Temperature | |||
-- | 74.0 | °C | ISO 306/B120 |
-- | 149 | °C | ISO 306/A120 |