SABIC PPcompound 1761高抗冲电池外壳级
Density | 0.900 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
Molding Shrinkage 1 (24 hr, 3.20 mm) | 1.1 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (Injection Molded) | 1200 | MPa | ISO 527-1/1A |
Tensile Stress | ISO 527-2/1A | ||
Yield, Injection Molded | 25.0 | MPa | |
Break, Injection Molded | 17.0 | MPa | |
Tensile Strain (Break, Injection Molded) | 45 | % | ISO 527-2/1A |
Flexural Modulus 2 (Injection Molded) | 1100 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact Strength | ISO 180/1A | ||
-20°C, Injection Molded | 4.0 | kJ/m² | |
23°C, Injection Molded | 50 | kJ/m² |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load 3 (1.8 MPa, Unannealed) | 88.0 | °C | ISO 75-2/A |