SABIC PPcompound 1961矿物增强高流动
Density | 0.00 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
Molding Shrinkage 1 (24 hr, 3.20 mm) | 1.0 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus (Injection Molded) | 2900 | MPa | ISO 527-1/1A |
Tensile Stress | ISO 527-2/1A | ||
Yield, Injection Molded | 35.0 | MPa | |
Break, Injection Molded | 30.0 | MPa | |
Tensile Strain (Break, Injection Molded) | 15 | % | ISO 527-2/1A |
Flexural Modulus 2 (Injection Molded) | 3000 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Notched Izod Impact Strength (23°C, Injection Molded) | 2.5 | kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load 3 | |||
0.45 MPa, Unannealed | 121 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 68.0 | °C | ISO 75-2/A |
Additional Information | Nominal Value | Unit | Test Method |
Filler Content | 20 | % | Internal Method |