Grivory XE 4095 black 9225 is a Polyamide 10T/X Copolymer (Nylon 10T/X) material filled with 50% glass fiber.
Density | 1.58 | -- | g/cm | ISO 1183 |
Molding Shrinkage | ISO 294-4 | |||
Across Flow | 0.70 | -- | % | |
Flow | 0.20 | -- | % | |
Water Absorption | ISO 62 | |||
Saturation, 23°C | 1.7 | -- | % | |
Equilibrium, 23°C, 50% RH | 0.80 | -- | % | |
| Hardness | Dry | Conditioned | Unit | Test Method |
Ball Indentation Hardness | 280 | 280 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 17000 | 16500 | MPa | ISO 527-2 |
Tensile Stress(Break) | 220 | 200 | MPa | ISO 527-2 |
Tensile Strain(Break) | 2.0 | 2.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | |||
-30°C | 10 | 10 | kJ/m | |
23°C | 11 | 11 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179/1eU | |||
-30°C | 75 | 70 | kJ/m | |
23°C | 80 | 70 | kJ/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
1.8 MPa, Unannealed | 270 | -- | °C | ISO 75-2/A |
8.0 MPa, Unannealed | 240 | -- | °C | ISO 75-2/C |
Continuous Use Temperature | ||||
--2 | 150 | -- | °C | ISO 2578 |
--3 | 250 | -- | °C | Internal Method |
Melting Temperature4 | 295 | -- | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | |||
Flow | 1.5E-5 | -- | cm/cm/°C | |
Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
Electric Strength | 32 | 31 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification | IEC 60695-11-10, -20 | |||
0.40 mm | HB | -- | ||
1.5 mm | HB | -- |
玻璃增强的PPA树脂有很高的HDT值，能耐受很高温度的短期作用，例如：在一个供炉中或者在蒸汽相和在红外逆流团结过程中。PPA树脂的热氧化稳定性使它能耐长期高温作用，玻璃增强级PPA，在20 000小时内，其连续使用温度可达330°F。